Effect of toothbrushing with different toothpastes at commercially pure titanium surface roughness / Efeito da escovação com diferentes dentifrícios na rugosidade superficial do titânio comercialmente puro
Renata Cristina Silveira RODRIGUES
Adriana Cláudia Lapria FARIA
Paulo Donato FRIGHETTO
Maria da Gloria Chiarello de MATTOS
Ricardo Faria RIBEIRO
Resumo
ABSTRACT
Objective
To evaluate the effect of brushing, using toothpastes with different fluoride concentrations, on the surface of commercially pure titanium (cp Ti).
Methods
Discs (13x4mm) made of cp Ti, embedded in PVC rings and metallographically polished have their surface roughness measured. Tooth brushing simulations (50,400 cycles) were performed: speed of 80mm/s, distance of 10mm distance, at 240 cycles/min. Three toothpastes were tested: Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) and Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), with 5000, 1300 and 500ppm fluoride concentrations, respectively. The brushings had 7.14g and 14.28g of toothpaste, both for 50ml of deionized water. The surface roughness was reevaluated and data were analyzed by two-way ANOVA and Tukey’s test for the effect of brushing and toothpastes.
Results
At the beginning, no significant difference (p=0.09) of roughness was noted among the experimental groups (Prevident, Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil): 0.160±0.019; Colgate Total 12 (Colgate-almolive Ind. e Com. Ltda., São Paulo, Brazil): 0.159±0.030; Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil): 0.157±0.019) but roughness decreased after the 1st (p<0.05) (0.094±0.010) and 2nd (0.089± 0.012) brushings (p<0.05) with Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), with no significant difference between the 1st and 2nd brushings (p=0.16). Discs brushed with Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) presented surface roughness similar (p=0.090) at the beginning and after the 1st brushing (0.133±0.029), and between the 1st and 2nd (0.113±0009) brushings (p=0.402); roughness after the 2nd brushing was statistically greater than at the beginning (p<0.05). Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) toothpaste caused a surface roughness significantly lower (p<0.05) after the 2nd brushing (0.113±0.010), compared to the 1st (0.147±0.020) and the starting point, which were statistically similar (p=0.090).
Conclusion
The results suggest that brushing using toothpastes with fluoride causes a decrease in the surface roughness of cp Ti, mainly when greater fluoride concentrations are present.
Indexing terms: Dentifrices. Fluorine. Titanium. Toothbrushing.
RESUMO
Objetivo
Avaliar o efeito da escovação com dentifrícios contendo diferentes concentrações de flúor na superfície do titânio comercialmente puro (Ti cp).
Métodos
Discos (13x4mm) de Ti cp, embutidos em anéis de PVC e polidos metalograficamente, tiveram a rugosidade superficial avaliada. A simulação da escovação (50400 ciclos) teve velocidade de 80mm/s, curso de 10mm, com 240 ciclos/min. Foram testados três dentifrícios: Prevident 5000, (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil); Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) e Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil), com 5000, 1300 e 500ppm de flúor, respectivamente. As escovações tiveram 7,14g e 14,28g de dentifrício, ambas para 50ml de água deionizada. A rugosidade superficial foi reavaliada e os dados analisados por ANOVA - dois fatores e teste de Tukey quanto ao efeito da escovação e dos dentifrícios.
Resultados
Inicialmente não houve diferença significante (p=0,09) na rugosidade dos grupos experimentais Prevident, (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,160±0,019; Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,159±0,030; Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,157±0,019), mas houve diminuição da rugosidade após a 1ª (0,094±0,010) (p<0,05) e 2ª 0,089±0,012) escovações (p<0,05) com Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil), sem diferença significativa entre as demais (p=0,16). Discos escovados com Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) apresentaram rugosidade semelhante inicialmente (p=0,090) e após a 1ª escovação (0,133± 0,029), e entre a 1ª e a 2ª escovações (0,113±0,009) (p=0,402); a rugosidade após a 2ª escovação foi significativamente maior que a inicial (p<0,05). O dentifrício Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) causou rugosidade superficial significativamente menor (p<0,05) após a 2ª escovação (0,113±0,010), comparada à 1ª (0,147±0,020) e a inicial, que foram semelhantes (p=0,090).
Conclusão
Os resultados sugerem que a escovação com dentifrícios fluoretados diminui a rugosidade superficial do Ti cp, mais significativamente quanto maiores as concentrações de flúor presentes.
Termos de indexação: Dentifrícios. Flúor. Titânio. Escovação dentária.
Texto completo: PDF
Adriana Cláudia Lapria FARIA
Paulo Donato FRIGHETTO
Maria da Gloria Chiarello de MATTOS
Ricardo Faria RIBEIRO
Resumo
ABSTRACT
Objective
To evaluate the effect of brushing, using toothpastes with different fluoride concentrations, on the surface of commercially pure titanium (cp Ti).
Methods
Discs (13x4mm) made of cp Ti, embedded in PVC rings and metallographically polished have their surface roughness measured. Tooth brushing simulations (50,400 cycles) were performed: speed of 80mm/s, distance of 10mm distance, at 240 cycles/min. Three toothpastes were tested: Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) and Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), with 5000, 1300 and 500ppm fluoride concentrations, respectively. The brushings had 7.14g and 14.28g of toothpaste, both for 50ml of deionized water. The surface roughness was reevaluated and data were analyzed by two-way ANOVA and Tukey’s test for the effect of brushing and toothpastes.
Results
At the beginning, no significant difference (p=0.09) of roughness was noted among the experimental groups (Prevident, Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil): 0.160±0.019; Colgate Total 12 (Colgate-almolive Ind. e Com. Ltda., São Paulo, Brazil): 0.159±0.030; Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil): 0.157±0.019) but roughness decreased after the 1st (p<0.05) (0.094±0.010) and 2nd (0.089± 0.012) brushings (p<0.05) with Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil), with no significant difference between the 1st and 2nd brushings (p=0.16). Discs brushed with Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) presented surface roughness similar (p=0.090) at the beginning and after the 1st brushing (0.133±0.029), and between the 1st and 2nd (0.113±0009) brushings (p=0.402); roughness after the 2nd brushing was statistically greater than at the beginning (p<0.05). Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brazil) toothpaste caused a surface roughness significantly lower (p<0.05) after the 2nd brushing (0.113±0.010), compared to the 1st (0.147±0.020) and the starting point, which were statistically similar (p=0.090).
Conclusion
The results suggest that brushing using toothpastes with fluoride causes a decrease in the surface roughness of cp Ti, mainly when greater fluoride concentrations are present.
Indexing terms: Dentifrices. Fluorine. Titanium. Toothbrushing.
RESUMO
Objetivo
Avaliar o efeito da escovação com dentifrícios contendo diferentes concentrações de flúor na superfície do titânio comercialmente puro (Ti cp).
Métodos
Discos (13x4mm) de Ti cp, embutidos em anéis de PVC e polidos metalograficamente, tiveram a rugosidade superficial avaliada. A simulação da escovação (50400 ciclos) teve velocidade de 80mm/s, curso de 10mm, com 240 ciclos/min. Foram testados três dentifrícios: Prevident 5000, (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil); Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) e Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil), com 5000, 1300 e 500ppm de flúor, respectivamente. As escovações tiveram 7,14g e 14,28g de dentifrício, ambas para 50ml de água deionizada. A rugosidade superficial foi reavaliada e os dados analisados por ANOVA - dois fatores e teste de Tukey quanto ao efeito da escovação e dos dentifrícios.
Resultados
Inicialmente não houve diferença significante (p=0,09) na rugosidade dos grupos experimentais Prevident, (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,160±0,019; Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,159±0,030; Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil): 0,157±0,019), mas houve diminuição da rugosidade após a 1ª (0,094±0,010) (p<0,05) e 2ª 0,089±0,012) escovações (p<0,05) com Prevident 5000 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil), sem diferença significativa entre as demais (p=0,16). Discos escovados com Colgate Total 12 (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) apresentaram rugosidade semelhante inicialmente (p=0,090) e após a 1ª escovação (0,133± 0,029), e entre a 1ª e a 2ª escovações (0,113±0,009) (p=0,402); a rugosidade após a 2ª escovação foi significativamente maior que a inicial (p<0,05). O dentifrício Tandy (Colgate-Palmolive Ind. e Com. Ltda., São Paulo, Brasil) causou rugosidade superficial significativamente menor (p<0,05) após a 2ª escovação (0,113±0,010), comparada à 1ª (0,147±0,020) e a inicial, que foram semelhantes (p=0,090).
Conclusão
Os resultados sugerem que a escovação com dentifrícios fluoretados diminui a rugosidade superficial do Ti cp, mais significativamente quanto maiores as concentrações de flúor presentes.
Termos de indexação: Dentifrícios. Flúor. Titânio. Escovação dentária.