Effect of dentin on the shear bond strength of different adhesive systems / Efeito do substrato dentinário na resistência de união ao cisalhamento de diferentes sistemas adesivos
Darlon Martins LIMA
Maria Salete Machado CANDIDO, in memorian
Resumo
Objective
This study assessed the shear bond strength of total-etch and self-etch adhesive systems to sound and caries-affected human dentin.
Methods
The total-etch adhesive systems investigated were Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) and Single Bond (3M ESPE, St. Paul, MN, USA), and the self-etch adhesive systems were Clearfill SE Bond (Kuraray, Osaka, Japan) and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Eighty human teeth were used, 40 sound and 40 caries-affected (n=10). They were cut with a diamond disc to expose the dentinal surface and the adhesion area was standardized to 4 millimeters. Caries detector was used on the caries-affected4 teeth and the affected tissue was removed. The bond shear strength of different adhesives was tested on sound dentin (control group) and caries-affected dentin (experimental group). Z-100 composite resin cylinders were fabricated using a two-piece mold, and the specimens were stored in distilled water at 37°C for 24 hours, and submitted to the shear strength bond test using a crosshead speed of 0.5 mm/min.
Results
The data were treated by analysis of variance and Tukey test and the significance level was set at 5%. Caries-affected dentin had a significant negative impact on the shear bond strength of total-etch adhesive systems.
Conclusion
Shear bond strength depends on dentin status and type of adhesive system used.
Indexing terms: Dentin. Dentin adhesives. Shear bond strength.
RESUMO
Objetivo
Avaliar a resistência de união ao cisalhamento de sistemas adesivos de condicionamento ácido total e autocondicionantes em dentina humana hígida e afetada por cárie.
Métodos
Os sistemas adesivos com etapa prévia de condicionamento ácido da estrutura dental utilizados foram: Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) e Single Bond (3M ESPE, St. Paul, MN, USA), e os sistemas adesivos autocondicionantes: Clearfill SE Bond (Kuraray, Osaka, Japan) e Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Foram utilizados 80 dentes humanos, sendo 40 hígidos e 40 cariados (n=10), cortados com disco de diamante, expondo a superfície de dentina, e a área de adesão padronizada, em 4 mm de diâmetro. Para os dentes cariados, após corte inicial, estes eram corados com solução evidenciadora de cárie, e o tecido corado removido. Nos Grupos controle, os sistemas adesivos eram aplicados em dentina hígida, e nos Grupos experimentais, aplicados em dentina afetada por cárie. Confeccionaram--se cilindros de resina composta Z-100, com auxílio de matriz bipartida, os corpos-de-prova obtidos, armazenados em água destilada a 37°C por 24 horas, e submetidos ao ensaio de cisalhamento, a uma velocidade de 0,5 mm/min.
Resultados
Foram submetidos à Análise de Variância, e ao teste de Tukey, ao nível de 5% de significância. Observou-se influência do fator substrato para os valores de resistência de união, diminuídos significantemente quando sistemas adesivos de condicionamento ácido total eram aplicados em dentina afetada por cárie.
Conclusão
O presente estudo indicou que a resistência de união ao cisalhamento é dependente do tipo de dentina e do tipo de sistema adesivo utilizado.
Termos de indexação: Dentina. Adesivos dentinários. Resistência ao cisalhamento.
Texto completo: PDF
Maria Salete Machado CANDIDO, in memorian
Resumo
Objective
This study assessed the shear bond strength of total-etch and self-etch adhesive systems to sound and caries-affected human dentin.
Methods
The total-etch adhesive systems investigated were Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) and Single Bond (3M ESPE, St. Paul, MN, USA), and the self-etch adhesive systems were Clearfill SE Bond (Kuraray, Osaka, Japan) and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Eighty human teeth were used, 40 sound and 40 caries-affected (n=10). They were cut with a diamond disc to expose the dentinal surface and the adhesion area was standardized to 4 millimeters. Caries detector was used on the caries-affected4 teeth and the affected tissue was removed. The bond shear strength of different adhesives was tested on sound dentin (control group) and caries-affected dentin (experimental group). Z-100 composite resin cylinders were fabricated using a two-piece mold, and the specimens were stored in distilled water at 37°C for 24 hours, and submitted to the shear strength bond test using a crosshead speed of 0.5 mm/min.
Results
The data were treated by analysis of variance and Tukey test and the significance level was set at 5%. Caries-affected dentin had a significant negative impact on the shear bond strength of total-etch adhesive systems.
Conclusion
Shear bond strength depends on dentin status and type of adhesive system used.
Indexing terms: Dentin. Dentin adhesives. Shear bond strength.
RESUMO
Objetivo
Avaliar a resistência de união ao cisalhamento de sistemas adesivos de condicionamento ácido total e autocondicionantes em dentina humana hígida e afetada por cárie.
Métodos
Os sistemas adesivos com etapa prévia de condicionamento ácido da estrutura dental utilizados foram: Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) e Single Bond (3M ESPE, St. Paul, MN, USA), e os sistemas adesivos autocondicionantes: Clearfill SE Bond (Kuraray, Osaka, Japan) e Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Foram utilizados 80 dentes humanos, sendo 40 hígidos e 40 cariados (n=10), cortados com disco de diamante, expondo a superfície de dentina, e a área de adesão padronizada, em 4 mm de diâmetro. Para os dentes cariados, após corte inicial, estes eram corados com solução evidenciadora de cárie, e o tecido corado removido. Nos Grupos controle, os sistemas adesivos eram aplicados em dentina hígida, e nos Grupos experimentais, aplicados em dentina afetada por cárie. Confeccionaram--se cilindros de resina composta Z-100, com auxílio de matriz bipartida, os corpos-de-prova obtidos, armazenados em água destilada a 37°C por 24 horas, e submetidos ao ensaio de cisalhamento, a uma velocidade de 0,5 mm/min.
Resultados
Foram submetidos à Análise de Variância, e ao teste de Tukey, ao nível de 5% de significância. Observou-se influência do fator substrato para os valores de resistência de união, diminuídos significantemente quando sistemas adesivos de condicionamento ácido total eram aplicados em dentina afetada por cárie.
Conclusão
O presente estudo indicou que a resistência de união ao cisalhamento é dependente do tipo de dentina e do tipo de sistema adesivo utilizado.
Termos de indexação: Dentina. Adesivos dentinários. Resistência ao cisalhamento.